SaabischeVertonPX08000hars iseen verbinding op basis van PA6-hars die Impact Modifier bevat.
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, breuk, 50 mm/min | 44 | MPa | ISO 527 |
| Tensielandeling, opbrengst, 50 mm/min | 3.9 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 78 | MPa | ISO 178 |
| Flexurale spanning, breuk, 2 mm/min | 6.7 | % | ISO 178 |
| Flexurale modulus, 2 mm/min | 1900 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboorde 80*10*4 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Termiek | Waarde | Eenheid | Standaard |
| CTE, 23°C tot 60°C, stroom | 1.02E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C tot 60°C, xflow | 9.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 151 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 57 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Schimmelkrimp, doorstroming | 1.4 | % | S-Plastics-methode |
| Waterabsorptie, 23°C/24 uur | 2.2 | % | ISO 62-1 |
| Bron GMD, laatstelijk bijgewerkt:05/21/2008 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 80 | °C |
| Droogtijd | 4 | uur |
| Maximaal vochtgehalte | 0.15 - 0.25 | % |
| Smelttemperatuur | 265 - 275 | °C |
| Voorkant - Temperatuur in zone 3 | 275 - 290 | °C |
| Midden - Temperatuur van zone 2 | 265 - 275 | °C |
| Temperatuur achterin zone 1 | 250 - 260 | °C |
| Schimmeltemperatuur | 80 - 95 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 30 - 60 | rpm |
| Bron GMD, laatstelijk bijgewerkt:05/21/2008 | ||
Andere gerelateerde producten die we aanbevelen:
Voor meer informatie downloadt u het gegevensblad | |
 | S-Plastics Verton PX08000.pdf |
Krijg het laatste citaat |