SaabischeGeloyFXTW28SKhars isWeerbestendige Geloy* XTW-hars in glinsterende VisualFX-kleur met verbeterde kras- en markeersprestaties.
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 44 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 37 | MPa | ASTM D 638 |
| Trekspanning, jaar, type I, 5 mm/min | 40 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 5 mm/min | 34 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 3 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 11 | % | ASTM D 638 |
| Tensile strain, yld, type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensielandeling, brk, type I, 5 mm/min | 9 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 2200 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 66 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2100 | MPa | ASTM D 790 |
| Tensiestress, rendement, 5 mm/min | 39 | MPa | ISO 527 |
| Trekspanning, breuk, 5 mm/min | 34 | MPa | ISO 527 |
| Tensiestress, rendement, 50 mm/min | 42 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 36 | MPa | ISO 527 |
| Tensielandeling, opbrengst, 5 mm/min | 3 | % | ISO 527 |
| Tenzij het voertuig niet meer dan 5 mm breekt. | 8 | % | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 3 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 9 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2200 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 61 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| Hardheid, H358/30 | 78 | MPa | ISO 2039-1 |
| Hardheid, Rockwell L | 68 | - | ISO 2039-2 |
| Hardheid, kust D | 71 | - | ISO 868 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 75 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 40 | J/m | ASTM D 256 |
| Multiaxiale impact | 32 | J | ISO 6603 |
| Totale energie van de instrumenteninslag, 23°C | 17 | J | ASTM D 3763 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 97 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 85 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 8.9E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 9.7E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 8.9E+01 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 9.7E+01 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, A/50 | 113 | °C | ISO 306 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 98 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 100 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 100 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.09 | - | ASTM D 792 |
| Schimmelkrimp, stroom, 3,2 mm | 0.4 - 0.7 | % | S-Plastics-methode |
| Smeltstroom, 260°C/5,0 kgf | 12 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.09 | g/cm3 | ISO 1183 |
| Smeltvolume, MVR bij 220°C/10,0 kg | 9 | cm3/10 min | ISO 1133 |
| Smeltvolume, MVR bij 260°C/5,0 kg | 11 | cm3/10 min | ISO 1133 |
| Smeltviscositeit, 260°C, 1500 sec-1 | 140 | Pa's | ISO 11443 |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| Voldoet aan UL, vlamklasse 94HB (3) | 1.6 | mm | UL 94 van GE |
| Bron GMD, laatstelijk bijgewerkt:07/31/2007 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 85 - 90 | °C |
| Droogtijd | 4 | uur |
| Droogtijd (cumulatief) | 8 | uur |
| Maximaal vochtgehalte | 0.04 | % |
| Smelttemperatuur | 240 - 270 | °C |
| Temperatuur van het spuitstuk | 220 - 255 | °C |
| Voorkant - Temperatuur in zone 3 | 230 - 260 | °C |
| Midden - Temperatuur van zone 2 | 220 - 255 | °C |
| Temperatuur achterin zone 1 | 215 - 250 | °C |
| Schimmeltemperatuur | 60 - 85 | °C |
| Achterdruk | 0.3 - 1 | MPa |
| Schroefsnelheid | 30 - 80 | rpm |
| Schot naar cilindergrootte | 40 - 80 | % |
| Afluchtsdiepte | 0.038 - 0.076 | mm |
| Bron GMD, laatstelijk bijgewerkt:07/31/2007 | ||
Andere gerelateerde producten die we aanbevelen:
|
Voor meer informatie downloadt u het gegevensblad |
|
 |
S-Plastics Geloy FXTW28SK.pdf |
|
Krijg het laatste citaat
Distributiebron van eerste rang in Zuid-China Vermindering van de aankoopkosten, verbetering van de aanbodstabiliteit, U helpen bij het vinden van de meest geschikte technische kunststofmaterialen
|