SaabischeXenoy.XL1339hars isGegevens gegenereerd in BOZ-laboratoria.
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 5 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 110 | % | ASTM D 638 |
| Tensielmodule, 50 mm/min | 2090 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 94 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2090 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | ASTM D 1044 |
| Tensiestress, rendement, 50 mm/min | 55 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 5 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 70 | % | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 80 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 699 | J/m | ASTM D 256 |
| Izod Impact, gesnoept, 0°C | 672 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -20°C | 598 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 245 | J/m | ASTM D 256 |
| Izod Impact, gesnoept, -40°C | 224 | J/m | ASTM D 256 |
| Izod Impact, ongeboorde 80*10*4 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ongeboorde 80*10*4 -30°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -10°C | 38 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekapst 80*10*4 -20°C | 35 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 25 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -40°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edge 80*10*4 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Termiek | Waarde | Eenheid | Standaard |
| CTE, -30°C tot 30°C, stroom | 7.56E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C tot 30°C, xflow | 7.92E-05 | 1/°C | ASTM D 696 |
| Warmtegeleidbaarheid | 0.18 | W/m-°C | ASTM C 177 |
| Vicat-verzachtingstemperatuur, A/50 | 140 | °C | ISO 306 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 130 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0,45 MPa Rand 120*10*4 sp=100 mm | 125 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Rand 120*10*4 sp=100mm | 105 | °C | ISO 75/Ae |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.22 | - | ASTM D 792 |
| Wateropname, 24 uur | 0.1 | % | ASTM D 570 |
| Waterabsorptie, evenwicht, 23C | 0.7 | % | ASTM D 570 |
| Waterabsorptie, 50% RH, evenwicht | 0.2 | % | ASTM D 570 |
| Schimmelkrimp op de trekbalk, stroom (2) | 0.5 tegen 0.8 | % | S-Plastics-methode |
| Schimmelkrimp op trekbalk, xflow (2) | 0.5 tegen 0.8 | % | S-Plastics-methode |
| Poisson's ratio | 0.4 | - | ASTM D 638 |
| Smeltvolume, MVR bij 265°C/1,2 kg | 4 | cm3/10 min | ISO 1133 |
| Elektrisch | Waarde | Eenheid | Standaard |
| Volumeweerstand | >1.E+14 | Ohm-cm | ASTM D 257 |
| Oppervlakteweerstand | >1.E+15 | Ohm. | ASTM D 257 |
| Dielectrische sterkte, in olie, 3,2 mm | 16.9 | kV/mm | ASTM D 149 |
| Relatieve doorlaatbaarheid, 50/60 Hz | 3.3 | - | ASTM D 150 |
| Relatieve doorlaatbaarheid, 1 MHz | 3.1 | - | ASTM D 150 |
| Dissipatiefactor, 50/60 Hz | 0.002 | - | ASTM D 150 |
| Dissipatiefactor, 1 MHz | 0.02 | - | ASTM D 150 |
| Bron GMD, laatstelijk bijgewerkt: 01/05/2000 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 110 | °C |
| Droogtijd | 4 - 6 | uur |
| Droogtijd (cumulatief) | 8 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 260 - 275 | °C |
| Temperatuur van het spuitstuk | 255 - 270 | °C |
| Voorkant - Temperatuur in zone 3 | 255 - 275 | °C |
| Midden - Temperatuur van zone 2 | 250 - 270 | °C |
| Temperatuur achterin zone 1 | 245 - 265 | °C |
| Schimmeltemperatuur | 65 - 90 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 50 - 80 | rpm |
| Schot naar cilindergrootte | 50 - 80 | % |
| Afluchtsdiepte | 0.013 - 0.02 | mm |
| Bron GMD, laatstelijk bijgewerkt: 01/05/2000 | ||
Met een sterk verkoopnetwerk en kracht, hebben we opslagdiensten in Guangzhou, Dongguan, Shenzhen vrijhandelszone,Hong Kong en vier andere plaatsen (conventionele productvoorraad hoger dan 1000 ton)We kunnen klanten voorzien van snelle reactie, professionele service en uitstekende producten!
|
Voor meer informatie downloadt u het gegevensblad |
|
|
S-Plastics Xenoy XL1339.pdf |
|
Krijg het laatste citaat
Distributiebron van eerste rang in Zuid-China Vermindering van de aankoopkosten, verbetering van de aanbodstabiliteit, U helpen bij het vinden van de meest geschikte technische kunststofmaterialen
|