SaabischeStat-konRE004hars iseen verbinding op basis van nylon 66 hars met koolstofvezel.
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, breuk | 219 | MPa | ASTM D 638 |
| Trekspanning, breek. | 4.3 | % | ASTM D 638 |
| Flexurale stress | 312 | MPa | ASTM D 790 |
| Flexurale module | 12340 | MPa | ASTM D 790 |
| Trekspanning, breuk | 233 | MPa | ISO 527 |
| Trekspanning, breek. | 2.9 | % | ISO 527 |
| Flexurale stress | 337 | MPa | ISO 178 |
| Flexurale module | 14600 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 523 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 64 | J/m | ASTM D 256 |
| Izod Impact, ongeboorde 80*10*4 +23°C | 54 | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Dichtheid | 1.25 | g/cm3 | ASTM D 792 |
| Elektrisch | Waarde | Eenheid | Standaard |
| Oppervlakteweerstand | 1.E+02 - 1.E+06 | Ohm. | ASTM D 257 |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| Voldoet aan UL, vlamklasse 94HB (3) | 1.5 | mm | UL 94 van GE |
| Bron GMD, laatstelijk bijgewerkt:10/01/2004 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 80 | °C |
| Droogtijd | 4 | uur |
| Maximaal vochtgehalte | 0.15 - 0.25 | % |
| Smelttemperatuur | 280 - 305 | °C |
| Voorkant - Temperatuur in zone 3 | 295 - 305 | °C |
| Midden - Temperatuur van zone 2 | 280 - 295 | °C |
| Temperatuur achterin zone 1 | 265 - 275 | °C |
| Schimmeltemperatuur | 95 - 110 | °C |
| Achterdruk | 0.2 - 0.3 | MPa |
| Schroefsnelheid | 30 - 60 | rpm |
| Bron GMD, laatstelijk bijgewerkt:10/01/2004 | ||
Andere gerelateerde producten die we aanbevelen:
Voor meer informatie kunt u het datasheet downloaden | |
 | S-Plastics Stat-kon RE004.pdf |
Krijg het laatste citaat |