SaabischeUltem MD131hars isTransparante, hoge stroom polyetherimide (Tg 217C).
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 5 mm/min | 105 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensielandeling, brk, type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 3590 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 167 | MPa | ASTM D 790 |
| Flexurele spanning, jaar, 2,6 mm/min, 100 mm span | 165 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 3550 | MPa | ASTM D 790 |
| Flexurale modulus, 2,6 mm/min, 100 mm span | 3520 | MPa | ASTM D 790 |
| Hardheid, Rockwell M. | 109 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Tensiestress, rendement, 50 mm/min | 105 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 85 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 6 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 60 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 160 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| Hardheid, H358/30 | 140 | MPa | ISO 2039-1 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 32 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 35 | J/m | ASTM D 256 |
| Izod Impact, achteruit gesnoept, 3,2 mm | 1174 | J/m | ASTM D 256 |
| Gardner, 23°C | 33 | J | S-Plastics-methode |
| Totale energie van de instrumenteninslag, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, ongeboorde 80*10*4 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ongeboorde 80*10*4 -30°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 218 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, niet gegrild | 205 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 197 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, niet gegrild | 207 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, niet gegrild | 198 | °C | ASTM D 648 |
| CTE, -40°C tot 150°C, stroom | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 150°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| Warmtegeleidbaarheid | 0.22 | W/m-°C | ASTM C 177 |
| Warmtegeleidbaarheid | 0.21 | W/m-°C | ISO 8302 |
| CTE, 23°C tot 150°C, stroom | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C tot 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Boldrukonderzoek, 125°C +/- 2°C | Pasjes | - | IEC 60695-10-2 |
| Vicat-verzachtingstemperatuur, A/50 | 215 | °C | ISO 306 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 211 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0,45 MPa Rand 120*10*4 sp=100 mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Rand 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.27 | - | ASTM D 792 |
| Wateropname, 24 uur | 0.25 | % | ASTM D 570 |
| Waterabsorptie, evenwicht, 23C | 1.25 | % | ASTM D 570 |
| Schimmelkrimp op de trekbalk, stroom (2) | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Schimmelkrimp, stroom, 3,2 mm | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Schimmelkrimp, xflow, 3,2 mm | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Smeltstroom, 337°C/6,6 kgf | 17.8 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.27 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 1.25 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Smeltvolume, MVR bij 340°C/5,0 kg | 13 | cm3/10 min | ISO 1133 |
| Smeltvolume, MVR bij 360°C/5,0 kg | 25 | cm3/10 min | ISO 1133 |
| Elektrisch | Waarde | Eenheid | Standaard |
| Volumeweerstand | 1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectrische sterkte, in de lucht, 1,6 mm | 32.6 | kV/mm | ASTM D 149 |
| Dielectrische sterkte, in olie, 1,6 mm | 27.9 | kV/mm | ASTM D 149 |
| Relatieve doorlaatbaarheid, 1 kHz | 3.15 | - | ASTM D 150 |
| Dissipatiefactor, 1 kHz | 0.0013 | - | ASTM D 150 |
| Dissipatiefactor, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Volumeweerstand | 1.E+15 | Ohm-cm | IEC 60093 |
| Oppervlakteweerstand, ROA | >1.E+15 | Ohm. | IEC 60093 |
| Dielectrische sterkte, in olie, 0,8 mm | 33 | kV/mm | IEC 60243-1 |
| Dielectrische sterkte, in olie, 1,6 mm | 25 | kV/mm | IEC 60243-1 |
| Dielectrische sterkte, in olie, 3,2 mm | 16 | kV/mm | IEC 60243-1 |
| Relatieve doorlaatbaarheid, 50/60 Hz | 2.9 | - | IEC 60250 |
| Relatieve doorlaatbaarheid, 1 MHz | 2.9 | - | IEC 60250 |
| Dissipatiefactor, 50/60 Hz | 0.0005 | - | IEC 60250 |
| Dissipatiefactor, 1 MHz | 0.006 | - | IEC 60250 |
| Dissipatiefactor, 2450 MHz | 0.0025 | - | IEC 60250 |
| Vergelijkende trackingindex | 150 | V | IEC 60112 |
| Vergelijkende trackingindex, M | 100 | V | IEC 60112 |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| Zuurstofindex (LOI) | 44 | % | ASTM D 2863 |
| Brandbaarheidsindex van gloeddraad 960°C, overschrijdt | 3.2 | mm | IEC 60695-2-12 |
| Zuurstofindex (LOI) | 47 | % | ISO 4589 |
| Bron GMD, laatstelijk bijgewerkt: 02/02/2006 | |||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 150 | °C |
| Droogtijd | 4 - 6 | uur |
| Droogtijd (cumulatief) | 24 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 350 - 400 | °C |
| Temperatuur van het spuitstuk | 345 - 400 | °C |
| Voorkant - Temperatuur in zone 3 | 345 - 400 | °C |
| Midden - Temperatuur van zone 2 | 340 - 400 | °C |
| Temperatuur achterin zone 1 | 330 - 400 | °C |
| Schimmeltemperatuur | 135 - 165 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 40 - 70 | rpm |
| Schot naar cilindergrootte | 40 - 60 | % |
| Afluchtsdiepte | 0.025 - 0.076 | mm |
| Bron GMD, laatstelijk bijgewerkt: 02/02/2006 | ||
Op voorraad met gunstige prijs
1.1000 serie
1000,MI9.0; 1010,MI18.0; Hu1000, medische kwaliteit.
2.2000-serie, toevoegen GF
2100, voeg 10% GF toe, MI 7.0;
2110, voeg 10% GF toe, MI 11.0;
2200, voeg 20% GF toe, MI 6.0;
2210, voeg 20% GF toe, MI 8.4;
2300, voeg 30% GF toe, MI 5.0;
2310, voeg 30% GF toe, MI 7.6;
3. andere
MD130, MD131, AUT195, ATX200, enz.;
In de afgelopen jaren hebben we de binnenlandse markt diepgaand verbouwd en actief buitenlandse markten verkend.Tot nu toe hebben we meer dan 1000 klanten van hoge kwaliteit producten en diensten geleverd in verschillende industrieën, waaronder: elektronica en elektrische apparaten, medische, voedsel,elektronica voor automobielindustrie, opto-elektronische communicatie, fotovoltaïsche nieuwe energie, waterbehandeling, vervoer en andere industrieën.
Samtion Chemical levert technische kunststoffen en speciale gemodificeerde materialen van S-Plastics en andere merken.met volledige kwalificaties en een superieure levercapaciteit en prijsvoordelen.
Alle producten hebben MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA certificaten!!
Met een sterk verkoopnetwerk en kracht, hebben we opslagdiensten in Guangzhou, Dongguan, Shenzhen vrijhandelszone,Hong Kong en vier andere plaatsen (conventionele productvoorraad hoger dan 1000 ton)We kunnen klanten voorzien van snelle reactie, professionele service en uitstekende producten!
|
Voor meer informatie downloadt u het gegevensblad |
|
|
S-Plastics Ultem MD131.pdf |
|
Krijg het laatste citaat
Distributiebron van eerste rang in Zuid-China Vermindering van de aankoopkosten, verbetering van de aanbodstabiliteit, U helpen bij het vinden van de meest geschikte technische kunststofmaterialen
|