SaabischeUltem HU1010hars isTransparante, verbeterde stroom Polyetherimide (Tg 217C). ECO Conform. Voor medische hulpmiddelen en farmaceutische toepassingen.Healthcare management of change, biocompatibel (ISO 10993 of USP Class VI),in contact met levensmiddelen- EtO en stoomsteriliseren.
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 5 mm/min | 105 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensielandeling, brk, type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 3580 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 174 | MPa | ASTM D 790 |
| Flexurele spanning, jaar, 2,6 mm/min, 100 mm span | 165 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 3420 | MPa | ASTM D 790 |
| Flexurale modulus, 2,6 mm/min, 100 mm span | 3510 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Tensiestress, rendement, 5 mm/min | 105 | MPa | ISO 527 |
| Trekspanning, breuk, 5 mm/min | 85 | MPa | ISO 527 |
| Tensielandeling, opbrengst, 5 mm/min | 6 | % | ISO 527 |
| Tenzij het voertuig niet meer dan 5 mm breekt. | 60 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 160 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 32 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 35 | J/m | ASTM D 256 |
| Gardner, 23°C | 33 | J | ASTM D 3029 |
| Totale energie van de instrumenteninslag, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 218 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, niet gegrild | 198 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, xflow | 5.E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C tot 150°C, stroom | 5.58E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 211 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 212 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 193 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.27 | - | ASTM D 792 |
| Schimmelkrimp, stroom, 3,2 mm | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Smeltstroom, 337°C/6,6 kgf | 17.8 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.27 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 1.25 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Smeltvolume, MVR bij 220°C/5,0 kg | 25 | cm3/10 min | ISO 1133 |
| Elektrisch | Waarde | Eenheid | Standaard |
| Volumeweerstand | 1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectrische sterkte, in de lucht, 1,6 mm | 32.6 | kV/mm | ASTM D 149 |
| Dielectrische sterkte, in olie, 1,6 mm | 27.9 | kV/mm | ASTM D 149 |
| Relatieve doorlaatbaarheid, 1 kHz | 3.15 | - | ASTM D 150 |
| Dissipatiefactor, 1 kHz | 0.0013 | - | ASTM D 150 |
| Dissipatiefactor, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Arc Resistance, wolfraam {PLC} | 5 | PLC-code | ASTM D 495 |
| Warmdraadontsteking {PLC) | 1 | PLC-code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC-code | UL 746A |
| Hoge ampere boog Ign, oppervlak {PLC} | 3 | PLC-code | UL 746A |
| Vergelijkende traceringsindex (UL) {PLC} | 4 | PLC-code | UL 746A |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| UL erkend, vlamklasse 94V-2 (3) | 0.71 | mm | UL 94 |
| UL erkend, vlamklasse 94V-0 (3) | 0.71 | mm | UL 94 |
| UL erkend, 94-5VA rating (3) | 2.99 | mm | UL 94 |
| Zuurstofindex (LOI) | 44 | % | ASTM D 2863 |
| Bron GMD, laatstelijk bijgewerkt:05/04/2007 | |||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 150 | °C |
| Droogtijd | 4 - 6 | uur |
| Droogtijd (cumulatief) | 24 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 350 - 400 | °C |
| Temperatuur van het spuitstuk | 345 - 400 | °C |
| Voorkant - Temperatuur in zone 3 | 345 - 400 | °C |
| Midden - Temperatuur van zone 2 | 340 - 400 | °C |
| Temperatuur achterin zone 1 | 330 - 400 | °C |
| Schimmeltemperatuur | 135 - 165 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 40 - 70 | rpm |
| Schot naar cilindergrootte | 40 - 60 | % |
| Afluchtsdiepte | 0.025 - 0.076 | mm |
| Bron GMD, laatstelijk bijgewerkt:05/04/2007 | ||
|
Voor meer informatie downloadt u het gegevensblad |
|
 |
S-Plastics Ultem HU1010.pdf |
|
Krijg het laatste citaat