SaabischeXenoy.1731Ahars isPBT+PC, goede impact, uitstekende fysieke eigendomsbehoud in automotive exteriors en OVAD.
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 60 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 60 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 5.6 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 108 | % | ASTM D 638 |
| Tensile strain, brk, type I, 10 mm/min | 240 | % | S-Plastics - Japan-methode |
| Tensielmodule, 5 mm/min | 2370 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 93 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2120 | MPa | ASTM D 790 |
| Tensiestress, rendement, 50 mm/min | 60 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 5 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 104 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2370 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 92 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2210 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 814 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 176 | J/m | ASTM D 256 |
| Izod Impact, gesnoept, 23°C, 6,4 mm | 160 | J/m | ASTM D 256 |
| Totale energie van de instrumenteninslag, 23°C | 58 | J | ASTM D 3763 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 59 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 16 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 65 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 13 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 130 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, niet gegrild | 110 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 92 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, niet gegrild | 120 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, niet gegrild | 105 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 8.32E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 8.35E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 8.32E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 8.35E-05 | 1/°C | ISO 11359-2 |
| Boldrukonderzoek, 75°C +/- 2°C | Passing | - | IEC 60695-10-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 130 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 131 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.22 | - | ASTM D 792 |
| Schimmelkrimp, stroom, 3,2 mm | 0.65 tegen 0.73 | % | S-Plastics-methode |
| Smeltstroom, 250°C/5,0 kgf | 9.6 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.22 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.28 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Smeltvolume, MVR bij 250°C/5,0 kg | 8 | cm3/10 min | ISO 1133 |
| Bron GMD, voor het laatst bijgewerkt:10/16/2006 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 110 | °C |
| Droogtijd | 4 - 6 | uur |
| Droogtijd (cumulatief) | 8 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 260 - 275 | °C |
| Temperatuur van het spuitstuk | 255 - 270 | °C |
| Voorkant - Temperatuur in zone 3 | 255 - 275 | °C |
| Midden - Temperatuur van zone 2 | 250 - 270 | °C |
| Temperatuur achterin zone 1 | 245 - 265 | °C |
| Schimmeltemperatuur | 65 - 90 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 50 - 80 | rpm |
| Schot naar cilindergrootte | 50 - 80 | % |
| Afluchtsdiepte | 0.013 - 0.02 | mm |
| Bron GMD, voor het laatst bijgewerkt:10/16/2006 | ||
Andere gerelateerde producten die we aanbevelen:
|
Voor meer informatie downloadt u het gegevensblad |
|
 |
S-Plastics Xenoy 1731A.pdf |
|