SaabischeCycoloy XCY480hars isHoge stroom
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 42 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 4 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 40 | % | ASTM D 638 |
| Tensielmodule, 50 mm/min | 2270 | MPa | ASTM D 638 |
| Tensielmodule, 5 mm/min | 2270 | MPa | ASTM D 638 |
| Flexurale stress | 73 | MPa | ASTM D 790 |
| Flexurale module | 2140 | MPa | ASTM D 790 |
| Tensiestress, rendement, 50 mm/min | 51 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 43 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 4 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 50 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 47 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 560 | J/m | ASTM D 256 |
| Izod Impact, gesnoept, 0°C | 450 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 260 | J/m | ASTM D 256 |
| Multiaxiale impact | 130 | J | ISO 6603 |
| Izod Impact, ingekerfd 80*10*3 +23°C | 55 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*3 0°C | 46 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*3 -30°C | 19 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 55 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 20 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| HDT, 0,45 MPa, 3,2 mm, niet gegrild | 117 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 95 | °C | ASTM D 648 |
| CTE, -30°C tot 80°C, stroom | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C tot 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, A/50 | 129 | °C | ISO 306 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 118 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 118 | °C | ISO 306 |
| HDT/Be, 0,45 MPa Rand 120*10*4 sp=100 mm | 118 | °C | ISO 75/Be |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Schimmelkrimp, doorstroming | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Smeltstroom, 260°C/5,0 kgf | 35 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.13 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.47 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Smeltvolume, MVR bij 260°C/2,16 kg | 12 | cm3/10 min | ISO 1133 |
| Smeltvolume, MVR bij 260°C/5,0 kg | 31 | cm3/10 min | ISO 1133 |
| Bron GMD, laatstelijk bijgewerkt:04/02/2008 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 90 - 100 | °C |
| Droogtijd | 2 - 4 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 240 - 270 | °C |
| Temperatuur van het spuitstuk | 220 - 260 | °C |
| Voorkant - Temperatuur in zone 3 | 230 - 270 | °C |
| Midden - Temperatuur van zone 2 | 230 - 270 | °C |
| Temperatuur achterin zone 1 | 210 - 240 | °C |
| Temperatuur van de hopper | 60 - 80 | °C |
| Schimmeltemperatuur | 60 - 90 | °C |
| Bron GMD, laatstelijk bijgewerkt:04/02/2008 | ||
|
Voor meer informatie downloadt u het gegevensblad |
|
 |