SaabischeCycolacMG8000SRhars is:
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 37 | MPa | ASTM D 638 |
| Trekspanning, jaar, type I, 5 mm/min | 51 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 5 mm/min | 34 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 3 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 9 | % | ASTM D 638 |
| Tensile strain, yld, type I, 5 mm/min | 2.8 | % | ASTM D 638 |
| Tensielandeling, brk, type I, 5 mm/min | 10 | % | ASTM D 638 |
| Tensielmodule, 50 mm/min | 2670 | MPa | ASTM D 638 |
| Tensielmodule, 5 mm/min | 2650 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 77 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2600 | MPa | ASTM D 790 |
| Hardheid, kust D | 78 | - | ASTM D 2240 |
| Tensiestress, rendement, 5 mm/min | 50 | MPa | ISO 527 |
| Trekspanning, breuk, 5 mm/min | 35 | MPa | ISO 527 |
| Tensiestress, rendement, 50 mm/min | 56 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 39 | MPa | ISO 527 |
| Tensielandeling, opbrengst, 5 mm/min | 2.8 | % | ISO 527 |
| Tenzij het voertuig niet meer dan 5 mm breekt. | 10 | % | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 3 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 8 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2600 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 80 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2700 | MPa | ISO 178 |
| Hardheid, H358/30 | 100 | MPa | ISO 2039-1 |
| Hardheid, Rockwell L | 87 | - | ISO 2039-2 |
| Test van de hardheid van het potlood, 1 kgf | HB | - | ASTM D 3363 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 80 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 60 | J/m | ASTM D 256 |
| Multiaxiale impact | 10 | J | ISO 6603 |
| Totale energie van de instrumenteninslag, 23°C | 25 | J | ASTM D 3763 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 13 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 89 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 83 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 8.7E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 8.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 8.7E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, A/50 | 98 | °C | ISO 306 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 91 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 92 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 87 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 77 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.06 | - | ASTM D 792 |
| Schimmelkrimp, stroom, 3,2 mm | 0.4 - 0.7 | % | S-Plastics-methode |
| Smeltstroom, 220°C/10,0 kgf | 25 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.07 | g/cm3 | ISO 1183 |
| Smeltvolume, MVR bij 220°C/10,0 kg | 25 | cm3/10 min | ISO 1133 |
| Smeltvolume, MVR bij 260°C/5,0 kg | 33 | cm3/10 min | ISO 1133 |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| Voldoet aan UL, vlamklasse 94HB (3) | 1.5 | mm | UL 94 van GE |
| Bron GMD, voor het laatst bijgewerkt:10/09/2007 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 75 - 85 | °C |
| Droogtijd | 2 - 4 | uur |
| Droogtijd (cumulatief) | 8 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 220 - 250 | °C |
| Temperatuur van het spuitstuk | 220 - 240 | °C |
| Voorkant - Temperatuur in zone 3 | 230 - 250 | °C |
| Midden - Temperatuur van zone 2 | 220 - 240 | °C |
| Temperatuur achterin zone 1 | 210 - 230 | °C |
| Schimmeltemperatuur | 40 - 80 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 60 | rpm |
| Schot naar cilindergrootte | 50 - 70 | % |
| Afluchtsdiepte | 0.038 - 0.051 | mm |
| Bron GMD, voor het laatst bijgewerkt:10/09/2007 | ||
Met een sterk verkoopnetwerk en kracht, hebben we opslagdiensten in Guangzhou, Dongguan, Shenzhen vrijhandelszone,Hong Kong en vier andere plaatsen (conventionele productvoorraad hoger dan 1000 ton)We kunnen klanten voorzien van snelle reactie, professionele service en uitstekende producten!
|
Voor meer informatie downloadt u het gegevensblad |
|
|
S-Plastics Cycolac MG8000SR.pdf |
|