S-Plastics ValoxIQ507hars: milieuvriendelijk, duurzaam en koolstofarm hars dat 30% glasvezel PBT+PC versterkt
Valox iQ507 biedt goede mechanische en thermische eigenschappen.
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 5 mm/min | 105 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 5 mm/min | 105 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 10 mm/min | 132 | MPa | S-Plastics - Japan-methode |
| Tensile strain, yld, type I, 5 mm/min | 1 | % | ASTM D 638 |
| Tensielandeling, brk, type I, 5 mm/min | 1 | % | ASTM D 638 |
| Tensile strain, brk, type I, 10 mm/min | 7 | % | S-Plastics - Japan-methode |
| Tensielmodule, 5 mm/min | 12800 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 196 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 9060 | MPa | ASTM D 790 |
| Hardheid, Rockwell R | 119 | - | ASTM D 785 |
| Tensiestress, rendement, 5 mm/min | 96 | MPa | ISO 527 |
| Trekspanning, breuk, 5 mm/min | 96 | MPa | ISO 527 |
| Tensielandeling, opbrengst, 5 mm/min | 1 | % | ISO 527 |
| Tenzij het voertuig niet meer dan 5 mm breekt. | 1 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 10200 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 187 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 8910 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 593 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 84 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 70 | J/m | ASTM D 256 |
| Totale energie van de instrumenteninslag, 23°C | 7 | J | ASTM D 3763 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 21 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 192 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 182 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 2.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 2.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 8.1E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 192 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 190 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 212 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 186 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.51 | - | ASTM D 792 |
| Schimmelkrimp, stroom, 3,2 mm | 0.1 - 0.4 | % | S-Plastics-methode |
| Schimmelkrimp, xflow, 3,2 mm | 0.4 - 0.8 | % | S-Plastics-methode |
| Smeltstroom, 250°C/5,0 kgf | 50 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.51 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.1 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Smeltvolume, MVR bij 220°C/5,0 kg | 43 | cm3/10 min | ISO 1133 |
| Smeltvolume, MVR bij 250°C/5,0 kg | 38 | cm3/10 min | ISO 1133 |
| Bron GMD, voor het laatst bijgewerkt:11/01/2007 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 120 | °C |
| Droogtijd | 3 - 4 | uur |
| Droogtijd (cumulatief) | 12 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 250 - 265 | °C |
| Temperatuur van het spuitstuk | 245 - 260 | °C |
| Voorkant - Temperatuur in zone 3 | 250 - 265 | °C |
| Midden - Temperatuur van zone 2 | 245 - 260 | °C |
| Temperatuur achterin zone 1 | 240 - 255 | °C |
| Schimmeltemperatuur | 65 - 90 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 50 - 80 | rpm |
| Schot naar cilindergrootte | 40 - 80 | % |
| Afluchtsdiepte | 0.025 - 0.038 | mm |
| Bron GMD, voor het laatst bijgewerkt:11/01/2007 | ||
|
Voor meer informatie downloadt u het gegevensblad |
|
 |
S-Plastics Valox IQ507.pdf |
|
Krijg het laatste citaat