S-Plastics Valox310SE0PBT-hars is een niet-versterkt, vlamvertragend PBT-injectiehars.
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 20 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 20 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 2820 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 101 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2620 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 19 | mg/1000cy | S-Plastics-methode |
| Tensiestress, rendement, 50 mm/min | 55 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 6 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 20 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2800 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 80 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2600 | MPa | ISO 178 |
| Hardheid, H358/30 | 105 | MPa | ISO 2039-1 |
| Hardheid, Rockwell R | 120 | - | ISO 2039-2 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 22 | J/m | ASTM D 256 |
| Totale energie van de instrumenteninslag, 23°C | 200 | J | ASTM D 3763 |
| Izod Impact, ongeboorde 80*10*4 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ongeboorde 80*10*4 -30°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Charpy Impact, gesnoept, 23°C | 4 | kJ/m2 | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edge 80*10*4 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 165 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 74 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, niet gegrild | 162 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, niet gegrild | 71 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C tot 138°C, stroom | 1.31E-04 | 1/°C | ASTM E 831 |
| Warmtegeleidbaarheid | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C tot 60°C, stroom | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C tot 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Boldrukonderzoek, 125°C +/- 2°C | Passages | - | IEC 60695-10-2 |
| Vicat-verzachtingstemperatuur, A/50 | 212 | °C | ISO 306 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 165 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 165 | °C | ISO 306 |
| HDT/Be, 0,45 MPa Rand 120*10*4 sp=100 mm | 135 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Rand 120*10*4 sp=100mm | 60 | °C | ISO 75/Ae |
| Relatieve temperatuurindex, Elec | 120 | °C | UL 746B |
| Relatieve temperatuurindex, Mech w/impact | 120 | °C | UL 746B |
| Relatieve temperatuurindex, Mech zonder impact | 140 | °C | UL 746B |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.4 | - | ASTM D 792 |
| Specifiek volume | 0.71 | cm3/g | ASTM D 792 |
| Schimmelkrimp op de trekbalk, stroom (2) | 1.1 - 1.8 | % | S-Plastics-methode |
| Schimmelkrimp, stroom, 3,2 mm | 1.5 - 2.3 | % | S-Plastics-methode |
| Schimmelkrimp, doorstroming, 0,75-2,3 mm | 0.9-1.6 | % | S-Plastics-methode |
| Schimmelkrimp, stroom, 2,3-4,6 mm | 1.5 - 2.3 | % | S-Plastics-methode |
| Schimmelkrimp op trekbalk, xflow (2) | 0.9-1.9 | % | S-Plastics-methode |
| Schimmelkrimp, xstroom, 0,75-2,3 mm | Een tot één.7 | % | S-Plastics-methode |
| Schimmelkrimp, xstroom, 2,3-4,6 mm | 1.6 - 2.4 | % | S-Plastics-methode |
| Smeltstroom, 250°C/2,16 kgf | 8.6 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.4 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.36 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Smeltvolume, MVR bij 250°C/2,16 kg | 8 | cm3/10 min | ISO 1133 |
| Elektrisch | Waarde | Eenheid | Standaard |
| Dielectrische sterkte, in de lucht, 3,2 mm | 18.4 | kV/mm | ASTM D 149 |
| Dielectrische sterkte, in olie, 1,6 mm | 22 | kV/mm | ASTM D 149 |
| Arc Resistance, wolfraam {PLC} | 6 | PLC-code | ASTM D 495 |
| Warmdraadontsteking {PLC) | 2 | PLC-code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC-code | UL 746A |
| Hoogspanningsboogweerstand {PLC) | 6 | PLC-code | UL 746A |
| Hoge ampere boog Ign, oppervlak {PLC} | 0 | PLC-code | UL 746A |
| Vergelijkende traceringsindex (UL) {PLC} | 3 | PLC-code | UL 746A |
| Volumeweerstand | >1.E+15 | Ohm-cm | IEC 60093 |
| Oppervlakteweerstand, ROA | >1.E+15 | Ohm. | IEC 60093 |
| Dielectrische sterkte, korte tijd, 1,0 mm | 18 | kV/mm | IEC 60243-1 |
| Dielectrische sterkte, in olie, 0,8 mm | 31 | kV/mm | IEC 60243-1 |
| Dielectrische sterkte, in olie, 1,6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectrische sterkte, in olie, 3,2 mm | 15 | kV/mm | IEC 60243-1 |
| Relatieve doorlaatbaarheid, 50/60 Hz | 2.9 | - | IEC 60250 |
| Relatieve doorlaatbaarheid, 100 Hz | 3.1 | - | IEC 60250 |
| Relatieve doorlaatbaarheid, 1 MHz | 2.8 | - | IEC 60250 |
| Dissipatiefactor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipatiefactor, 100 Hz | 0.002 | - | IEC 60250 |
| Dissipatiefactor, 1 MHz | 0.01 | - | IEC 60250 |
| Vergelijkende trackingindex | 175 | V | IEC 60112 |
| Vergelijkende trackingindex, M | 100 | V | IEC 60112 |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| UL erkend, vlamklasse 94V-0 (3) | 0.71 | mm | UL 94 |
| UL erkend, 94-5VA rating (3) | 3 | mm | UL 94 |
| Brandbaarheidsindex van gloeddraad 960°C, overschrijdt | 1 | mm | IEC 60695-2-12 |
| Zuurstofindex (LOI) | 30 | % | ISO 4589 |
| Bron GMD, voor het laatst bijgewerkt:07/27/2007 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 120 | °C |
| Droogtijd | 3 - 4 | uur |
| Droogtijd (cumulatief) | 12 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 245 - 260 | °C |
| Temperatuur van het spuitstuk | 240 - 255 | °C |
| Voorkant - Temperatuur in zone 3 | 245 - 260 | °C |
| Midden - Temperatuur van zone 2 | 240 - 255 | °C |
| Temperatuur achterin zone 1 | 230 - 250 | °C |
| Schimmeltemperatuur | 50 - 75 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 50 - 100 | rpm |
| Schot naar cilindergrootte | 40 - 80 | % |
| Afluchtsdiepte | 0.013 - 0.025 | mm |
| Bron GMD, voor het laatst bijgewerkt:07/27/2007 | ||
Warm verkoopproduct (op voorraad)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT +glas gevuld: DR51, DR48, 420 420se0, 553, 508, 420 pk
Met een sterk verkoopnetwerk en kracht, hebben we opslagdiensten in Guangzhou, Dongguan, Shenzhen vrijhandelszone,Hong Kong en vier andere plaatsen (conventionele productvoorraad hoger dan 1000 ton)We kunnen klanten voorzien van snelle reactie, professionele service en uitstekende producten!
|
Voor meer informatie downloadt u het gegevensblad |
|
|