S-Plastics Lubricomp DX98306Hhars is
| Typische eigenschappen(1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, opbrengst | 51 | MPa | ASTM D 638 |
| Trekspanning, breuk | 42 | MPa | ASTM D 638 |
| Trekspanning, jaar, type I, 5 mm/min | 0 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 5 mm/min | 43 | MPa | ASTM D 638 |
| Tensile Spanning, opbrengst | 5.3 | % | ASTM D 638 |
| Trekspanning, breek. | 32.8 | % | ASTM D 638 |
| Tensile strain, yld, type I, 5 mm/min | 0 | % | ASTM D 638 |
| Tensielandeling, brk, type I, 5 mm/min | 2.3 | % | ASTM D 638 |
| Tensielmodule, 50 mm/min | 2060 | MPa | ASTM D 638 |
| Tensielmodule, 5 mm/min | 5090 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 85 | MPa | ASTM D 790 |
| Flexurale module | 2060 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 5010 | MPa | ASTM D 790 |
| Trekspanning, opbrengst | 51 | MPa | ISO 527 |
| Trekspanning, breuk | 43 | MPa | ISO 527 |
| Tensiestress, rendement, 5 mm/min | 0 | MPa | ISO 527 |
| Trekspanning, breuk, 5 mm/min | 48 | MPa | ISO 527 |
| Tensile Spanning, opbrengst | 5.3 | % | ISO 527 |
| Trekspanning, breek. | 38.2 | % | ISO 527 |
| Tensielandeling, opbrengst, 5 mm/min | 0 | % | ISO 527 |
| Tenzij het voertuig niet meer dan 5 mm breekt. | 2.3 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2140 | MPa | ISO 527 |
| Flexurale stress | 71 | MPa | ISO 178 |
| Flexurele spanning, rendement, 2 mm/min | 90 | MPa | ISO 178 |
| Flexurale module | 2100 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 5120 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 1767 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 154 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 69 | J/m | ASTM D 256 |
| Geïnstrumenteerde slagenergie @ piek, 23°C | 34 | J | ASTM D 3763 |
| Multiaxiale impact | 32 | J | ISO 6603 |
| Totale energie van de instrumenteninslag, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, ongeboorde 80*10*4 +23°C | 180 | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*4 +23°C | 13 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 141 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, niet gegrild | 132 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 122 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 7.56E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 7.38E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 7.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 141 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 145 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 123 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.48 | - | ASTM D 792 |
| Dichtheid | 1.29 | g/cm3 | ASTM D 792 |
| Vochtopname, 50% RH, 24 uur | 0.1 | % | ASTM D 570 |
| Schimmelkrimp, stroom, 3,2 mm | 0.3 - 0.5 | % | S-Plastics-methode |
| Schimmelkrimp, doorstroming, 24 uur | 0.5 tegen 0.7 | % | ASTM D 955 |
| Schimmelkrimp, xflow, 24 uur | 0.6 - 0.8 | % | ASTM D 955 |
| Schimmelkrimp, doorstroming, 24 uur | 0.64 | % | ISO 294 |
| Schimmelkrimp, xflow, 24 uur | 0.74 | % | ISO 294 |
| Smeltstroom, 300°C/1,2 kgf | 8.5 | g/10 min | ASTM D 1238 |
| Draagfactor wasmachine | 21 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Gewijzigd |
| Dynamische COF | 0.37 | - | ASTM D 3702 Gewijzigd |
| Statische COF | 0.32 | - | ASTM D 3702 Gewijzigd |
| Dichtheid | 1.29 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.2 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Smeltvolume, MVR bij 300°C/1,2 kg | 6 | cm3/10 min | ISO 1133 |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| UL erkend, vlamklasse 94HB (3) | 0.7 | mm | UL 94 |
| Bron GMD, voor het laatst bijgewerkt: 09/24/2008 | |||
Verwerking
| Parameter | |||
| Injectievorming | Waarde | Eenheid | |
| Droogtemperatuur | 120 | °C | |
| Droogtijd | 4 | uur | |
| Maximaal vochtgehalte | 0.02 | % | |
| Smelttemperatuur | 300 - 315 | °C | |
| Voorkant - Temperatuur in zone 3 | 310 - 320 | °C | |
| Midden - Temperatuur van zone 2 | 305 - 315 | °C | |
| Temperatuur achterin zone 1 | 295 - 305 | °C | |
| Schimmeltemperatuur | 80 - 110 | °C | |
| Achterdruk | 0.2 - 0.3 | MPa | |
| Schroefsnelheid | 30 - 60 | rpm | |
| Bron GMD, voor het laatst bijgewerkt: 09/24/2008 | |||
In de afgelopen jaren hebben we de binnenlandse markt diepgaand verbouwd en actief buitenlandse markten verkend.Tot nu toe hebben we meer dan 1000 klanten van hoge kwaliteit producten en diensten geleverd in verschillende industrieën, waaronder: elektronica en elektrische apparaten, medische, voedsel,elektronica voor automobielindustrie, opto-elektronische communicatie, fotovoltaïsche nieuwe energie, waterbehandeling, vervoer en andere industrieën.
Samtion Chemical levert technische kunststoffen en speciale gemodificeerde materialen van S-Plastics en andere merken.met volledige kwalificaties en een superieure levercapaciteit en prijsvoordelen.
Alle producten hebben MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA certificaten!!
Andere gerelateerde producten die we aanbevelen:
|
Voor meer informatie kunt u het datasheet downloaden |
|
 |