SaabischeThermocompAF006XXZhars iseen verbinding op basis van acrylonitril-butadiene-styreenhars die glasvezels bevat.
| Typische eigenschappen (1) | |||
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, breuk | 96 | MPa | ASTM D 638 |
| Trekspanning, breek. | 1.8 | % | ASTM D 638 |
| Flexurale stress | 153 | MPa | ASTM D 790 |
| Flexurale module | 9170 | MPa | ASTM D 790 |
| Trekspanning, breuk | 83 | MPa | ISO 527 |
| Trekspanning, breek. | 1.7 | % | ISO 527 |
| Flexurale stress | 119 | MPa | ISO 178 |
| Flexurale module | 8000 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 58 | J/m | ASTM D 256 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termiek | Waarde | Eenheid | Standaard |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 102 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Dichtheid | 1.28 | g/cm3 | ASTM D 792 |
| Schimmelkrimp, doorstroming, 24 uur | 0.2 | % | ASTM D 955 |
| Schimmelkrimp, xflow, 24 uur | 0.4 | % | ASTM D 955 |
| Bron GMD, laatstelijk bijgewerkt:10/01/2004 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 80 | °C |
| Droogtijd | 4 | uur |
| Maximaal vochtgehalte | 0.05 tegen 0.1 | % |
| Smelttemperatuur | 260 | °C |
| Voorkant - Temperatuur in zone 3 | 265 - 275 | °C |
| Midden - Temperatuur van zone 2 | 230 - 245 | °C |
| Temperatuur achterin zone 1 | 205 - 215 | °C |
| Schimmeltemperatuur | 70 - 80 | °C |
| Achterdruk | 0.2 - 0.3 | MPa |
| Schroefsnelheid | 30 - 60 | rpm |
| Bron GMD, laatstelijk bijgewerkt:10/01/2004 | ||