| Trekspanning, jaar, type I, 50 mm/min |
63 |
MPa |
ASTM D638 |
| Tensile strain, yld, type I, 50 mm/min |
6 |
% |
ASTM D638 |
| Strekkingsspanning, brk, type I, 50 mm/min |
> 70 |
% |
ASTM D638 |
| Tensielmodule, 50 mm/min |
2350 |
MPa |
ASTM D638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span |
90 |
MPa |
ASTM D790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning |
2300 |
MPa |
ASTM D790 |
| Hardheid, Rockwell R |
120 |
- |
ASTM D785 |
| Tensiestress, rendement, 50 mm/min |
63 |
MPa |
ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min |
6 |
% |
ISO 527 |
| Tensile spanning, breuk, 50 mm/min. |
> 70 |
% |
ISO 527 |
| Tensielmodule, 1 mm/min |
2350 |
MPa |
ISO 527 |
| Flexurele spanning, rendement, 2 mm/min |
90 |
MPa |
ISO 178 |
| Flexurale modulus, 2 mm/min |
2300 |
MPa |
ISO 178 |
| Hardheid, Rockwell R |
120 |
- |
ISO 2039-2 |
| INKOMST |
|
|
|
| Izod Impact, ongeboord, 23°C |
NB: |
J/m |
ASTM D4812 |
| Izod Impact, gesnoept, 23°C |
900 |
J/m |
ASTM D256 |
| Geïnstrumenteerde slagenergie @ piek, 23°C |
65 |
J |
ASTM D3763 |
| Izod Impact, ongeboorde 80*10*3 +23°C |
NB: |
kJ/m2 |
ISO 180/1U |
| Izod Impact, ongeboord 80*10*3 -30°C |
NB: |
kJ/m2 |
ISO 180/1U |
| Izod Impact, ingekerfd 80*10*3 +23°C |
70 |
kJ/m2 |
ISO 180/1A |
| Izod Impact, ingekerfd 80*10*3 -30°C |
12 |
kJ/m2 |
ISO 180/1A |
| Termiek |
|
|
|
| Vicat-verzachtingstemperatuur, snelheid B/50 |
144 |
°C |
ASTM D1525 |
| HDT, 0,45 MPa, 3,2 mm |
138 |
°C |
ASTM D648 |
| HDT, 1,82 MPa, 3,2 mm |
127 |
°C |
ASTM D648 |
| CTE, -40 °C tot 95 °C, stroom |
7.00E-05 |
1/°C |
ASTM E831 |
| Warmtegeleidbaarheid |
0.2 |
W/m-°C |
ASTM C177 |
| Warmtegeleidbaarheid |
0.2 |
W/m-°C |
ISO 8302 |
| CTE, 23°C tot 80°C, stroom |
7.00E-05 |
1/°C |
ISO 11359-2 |
| Boldrukonderzoek, 125°C +/- 2°C |
Pasjes |
- |
IEC 60695-10-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 |
144 |
°C |
ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm |
138 |
°C |
ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm |
127 |
°C |
ISO 75/Af |
| FYSISCHE |
|
|
|
| Specifieke zwaarte |
1.2 |
- |
ASTM D792 |
| Wateropname (23°C/verzadigd) |
0.35 |
% |
ASTM D570 |
| Schimmelkrimp op de trekbalk, stroom |
0.5-0.7 |
% |
S-Plastics-methode |
| Schimmelkrimp, stroom, 3,2 mm |
0.5-0.7 |
% |
S-Plastics-methode |
| Smeltstroom, 300°C/1,2 kgf |
7 |
g/10 min |
ASTM D1238 |
| Dichtheid |
1.2 |
g/cm3 |
ISO 1183 |
| Wateropname (23°C/verzadigd) |
0.35 |
% |
ISO 62-1 |
| Smeltvolume, MVR bij 300°C/1,2 kg |
6 |
cm3/10 min |
ISO 1133 |
| Optische |
|
|
|
| Lichttransmissie, 2,54 mm |
88-90 |
% |
ASTM D1003 |
| Nevel, 2,54 mm |
< 0.8 |
% |
ASTM D1003 |
| Brekingsindex |
1.586 |
- |
ASTM D542 |
| Brekingsindex |
1.586 |
- |
ISO 489 |
| Elektrisch |
|
|
|
| Volumeweerstand |
>1.E+15 |
Ω.cm |
ASTM D257 |
| Dielectrische sterkte, 1,6 mm |
27 |
kV/mm |
ASTM D149 |
| Relatieve doorlaatbaarheid, 60 Hz |
3 |
- |
ASTM D150 |
| Relatieve doorlaatbaarheid, 1 MHz |
3 |
- |
ASTM D150 |
| Dissipatiefactor, 60 Hz |
0.001 |
- |
ASTM D150 |
| Dissipatiefactor, 1 MHz |
0.01 |
- |
ASTM D150 |
| Volumeweerstand |
>1.E+15 |
Ω.cm |
IEC 60093 |
| Dielectrische sterkte, 1,6 mm |
27 |
kV/mm |
IEC 60243-1 |
| Relatieve doorlaatbaarheid, 60 Hz |
3 |
- |
IEC 60250 |
| Relatieve doorlaatbaarheid, 1 MHz |
3 |
- |
IEC 60250 |
| Dissipatiefactor, 60 Hz |
0.001 |
- |
IEC 60250 |
| Dissipatiefactor, 1 MHz |
0.01 |
- |
IEC 60250 |
| Vlamkenkenmerken |
|
|
|
| UL Yellow Card Link |
E207780-101295396 |
- |
- |
| UL erkend, vlamklasse 94V-2 |
1.6 |
mm |
UL 94 |
|
|
|
|