SaabischeLexanHP2JPHars is Med/high flow polycarbonaat. Voor medische hulpmiddelen en farmaceutische toepassingen. Healthcare management of change, biocompatibel ((ISO10993 of USP Class VI). EtO en stoomsteriliserbaar.Bevat schimmelvrijstelling.
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 68 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 7 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 125 | % | ASTM D 638 |
| Tensielmodule, 50 mm/min | 2370 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 96 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2340 | MPa | ASTM D 790 |
| Hardheid, Rockwell M. | 70 | - | ASTM D 785 |
| Hardheid, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Tensiestress, rendement, 50 mm/min | 63 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 6 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 100 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 90 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, ongeboord, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Impact, gesnoept, 23°C | 694 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | NA | J/m | ASTM D 256 |
| Tensile impact, type S. | 546 | kJ/m2 | ASTM D 1822 |
| Inval van de pijl (D 3029), 23°C | 169 | J | ASTM D 3029 |
| Totale energie van de instrumenteninslag, 23°C | 633 | J | ASTM D 3763 |
| Izod Impact, ingekerfd 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NA | kJ/m2 | ISO 179/1eU |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 154 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, niet gegrild | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, niet gegrild | 129 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, xflow | 6.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40 °C tot 95 °C, stroom | 6.84E-05 | 1/°C | ASTM E 831 |
| Specifieke warmte | 1.25 | J/g-°C | ASTM C 351 |
| Warmtegeleidbaarheid | 0.19 | W/m-°C | ASTM C 177 |
| CTE, -40°C tot 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C tot 80°C, stroom | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 140 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 141 | °C | ISO 306 |
| Relatieve temperatuurindex, Elec | 130 | °C | UL 746B |
| Relatieve temperatuurindex, Mech w/impact | 130 | °C | UL 746B |
| Relatieve temperatuurindex, Mech zonder impact | 130 | °C | UL 746B |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.2 | - | ASTM D 792 |
| Specifiek volume | 0.83 | cm3/g | ASTM D 792 |
| Dichtheid | 1.19 | g/cm3 | ASTM D 792 |
| Wateropname, 24 uur | 0.15 | % | ASTM D 570 |
| Waterabsorptie, evenwicht, 23C | 0.35 | % | ASTM D 570 |
| Waterabsorptie, evenwicht, 100°C | 0.58 | % | ASTM D 570 |
| Schimmelkrimp, stroom, 3,2 mm | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Smeltstroom, 300°C/1,2 kgf | 17.5 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.2 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.35 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Smeltvolume, MVR bij 300°C/1,2 kg | 16 | cm3/10 min | ISO 1133 |
| Optische | Waarde | Eenheid | Standaard |
| Lichttransmissie | 88 | % | ASTM D 1003 |
| Nevel | 1 | % | ASTM D 1003 |
| Brekingsindex | 1.586 | - | ASTM D 542 |
| Elektrisch | Waarde | Eenheid | Standaard |
| Volumeweerstand | >1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectrische sterkte, in de lucht, 3,2 mm | 14.9 | kV/mm | ASTM D 149 |
| Relatieve doorlaatbaarheid, 50/60 Hz | 3.17 | - | ASTM D 150 |
| Relatieve doorlaatbaarheid, 1 MHz | 2.96 | - | ASTM D 150 |
| Dissipatiefactor, 50/60 Hz | 0.0009 | - | ASTM D 150 |
| Dissipatiefactor, 1 MHz | 0.01 | - | ASTM D 150 |
| Warmdraadontsteking {PLC) | 2 | PLC-code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC-code | UL 746A |
| Hoge ampere boog Ign, oppervlak {PLC} | 1 | PLC-code | UL 746A |
| Vergelijkende traceringsindex (UL) {PLC} | 2 | PLC-code | UL 746A |
| Vlamkenkenmerken | Waarde | Eenheid | Standaard |
| UL erkend, vlamklasse 94HB (3) | 1.47 | mm | UL 94 |
| Bron GMD, voor het laatst bijgewerkt: 02/16/2007 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 120 | °C |
| Droogtijd | 3 - 4 | uur |
| Droogtijd (cumulatief) | 48 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 280 - 305 | °C |
| Temperatuur van het spuitstuk | 275 - 300 | °C |
| Voorkant - Temperatuur in zone 3 | 280 - 305 | °C |
| Midden - Temperatuur van zone 2 | 270 - 295 | °C |
| Temperatuur achterin zone 1 | 260 - 280 | °C |
| Schimmeltemperatuur | 70 - 95 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 40 - 70 | rpm |
| Schot naar cilindergrootte | 40 - 60 | % |
| Afluchtsdiepte | 0.025 - 0.076 | mm |
| Bron GMD, voor het laatst bijgewerkt: 02/16/2007 | ||
|
Voor meer informatie downloadt u het gegevensblad |
|
 |
S-Plastics Lexan HP2JP.pdf |
|
Krijg het laatste citaat
Distributiebron van eerste rang in Zuid-China Vermindering van de aankoopkosten, verbetering van de aanbodstabiliteit, U helpen bij het vinden van de meest geschikte technische kunststofmaterialen
|
|