SaabischeLexanHP2EU Hars is Med/high flow polycarbonaat. Voor medische hulpmiddelen en farmaceutische toepassingen. Healthcare management of change, biocompatibel ((ISO10993 of USP Class VI). EtO en stoomsteriliserbaar.Bevat schimmelvrijstelling.
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 630 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 700 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 7 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 125 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 630 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 980 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2350 | MPa | ASTM D 790 |
| Tensiestress, rendement, 50 mm/min | 63 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 6 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 100 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 90 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 70 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 30 | J/m | ASTM D 256 |
| Totale energie van de instrumenteninslag, 23°C | 633 | J | ASTM D 3763 |
| Izod Impact, ongeboorde 80*10*3 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ongeboord 80*10*3 -30°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*3 +23°C | 60 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*3 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Charpy Impact, gesnoept, 23°C | 35 | kJ/m2 | ISO 179/2C |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 139 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 129 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 6.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 6.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C tot 80°C, stroom | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 140 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 141 | °C | ISO 306 |
| HDT/Be, 0,45 MPa Rand 120*10*4 sp=100 mm | 133 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Rand 120*10*4 sp=100mm | 122 | °C | ISO 75/Ae |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.2 | - | ASTM D 792 |
| Schimmelkrimp op de trekbalk, stroom (2) | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Schimmelkrimp, stroom, 3,2 mm | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Smeltstroom, 300°C/1,2 kgf | 22 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.2 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.35 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Smeltvolume, MVR bij 300°C/1,2 kg | 21 | cm3/10 min | ISO 1133 |
| Optische | Waarde | Eenheid | Standaard |
| Lichttransmissie | 88 | % | ASTM D 1003 |
| Nevel | < 0.8 | % | ASTM D 1003 |
| Bron GMD, laatstelijk bijgewerkt: 03/15/2007 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 120 | °C |
| Droogtijd | 2 - 4 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 280 - 300 | °C |
| Temperatuur van het spuitstuk | 270 - 290 | °C |
| Voorkant - Temperatuur in zone 3 | 280 - 300 | °C |
| Midden - Temperatuur van zone 2 | 270 - 290 | °C |
| Temperatuur achterin zone 1 | 260 - 280 | °C |
| Temperatuur van de hopper | 60 - 80 | °C |
| Schimmeltemperatuur | 80 - 100 | °C |
| Bron GMD, laatstelijk bijgewerkt: 03/15/2007 | ||
|