SaabischeLexanHFD1830 (2)Hars is 40 MFR High Flow Ductile Copolymer UV gestabiliseerd
| Mechanische | Typische waarden | Eenheden | Testmethoden |
| Trekspanning, jaar, type I, 50 mm/min | 60 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 5.5 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 130 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 2270 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 100 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2240 | MPa | ASTM D 790 |
| Hardheid, Rockwell R | 120 | - | ASTM D 785 |
| Tensiestress, rendement, 50 mm/min | 63 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 6 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 97 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2180 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 91 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2180 | MPa | ISO 178 |
| INKOMST | |||
| Izod Impact, gesnoept, 23°C | 728 | J/m | ASTM D 256 |
| Izod Impact, gesnoept, 0°C | 699 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 115 | J/m | ASTM D 256 |
| Multiaxiale impact | 95 | J | ISO 6603 |
| Totale energie van de instrumenteninslag, 23°C | 56 | J | ASTM D 3763 |
| Izod Impact, ongeboorde 80*10*3 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ongeboord 80*10*3 -30°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*3 +23°C | 58 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*3 -30°C | 11 | kJ/m2 | ISO 180/1A |
| © 2017 Copyright door S-Plastics. Alle rechten voorbehouden. | |||
| Vastgoed | Typische waarden | Eenheden | Testmethoden |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 64 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 13 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Termiek | |||
| Vicat-verzachtingstemperatuur, snelheid B/50 | 135 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, niet gegrild | 121 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 110 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Boldrukonderzoek, 125°C +/- 2°C | Passing | - | IEC 60695-10-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 129 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 130 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 115 | °C | ISO 75/Af |
| FYSISCHE | |||
| Specifieke zwaarte | 1.2 | - | ASTM D 792 |
| Dichtheid | 1.2 | g/cm3 | ASTM D 792 |
| Schimmelkrimp, doorstroming, 3,2 mm (5) | 0.5 ¢ 0.7 | % | S-Plastics-methode |
| Smeltstroom, 300°C/1,2 kgf | 40 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.2 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.3 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Smeltvolume, MVR bij 300°C/1,2 kg | 38 | cm3/10 min | ISO 1133 |
| Optische | |||
| Lichttransmissie, 2,54 mm | 88 | % | ASTM D 1003 |
| Nevel, 2,54 mm | < 1 | % | ASTM D 1003 |
| Brekingsindex | 1.582 | - | ASTM D542 |
| Injectievorming | |||
| Droogtemperatuur | 105 ¢ 110 | °C | |
| Droogtijd | 3 4 | uur | |
| Droogtijd (cumulatief) | 24 | uur | |
| Smelttemperatuur | 260 ¢ 305 | °C | |
| Temperatuur van het spuitstuk | 255 ¢ 300 | °C | |
| Voorkant - Temperatuur in zone 3 | 260 ¢ 305 | °C | |
| Midden - Temperatuur van zone 2 | 250,295 | °C | |
| Temperatuur achterin zone 1 | 240 ¢ 280 | °C | |
| © 2017 Copyright door S-Plastics. Alle rechten voorbehouden. | |||
| Vastgoed | Typische waarden | Eenheden | Testmethoden |
| Schimmeltemperatuur | 50 ¢ 80 | °C | |
| Achterdruk | 0.3 ¢ 0.7 | MPa | |
| Schroefsnelheid | 35 ¢ 75 | rpm | |
| Schot naar cilindergrootte | 40 ¢ 60 | % | |
| Afluchtsdiepte | 0.038 ¢ 0.076 | mm |
|