SaabischeLexanHFD1212hars is 18 MFR High Flow Ductile Copolymer
| Mechanische | Waarde | Eenheid | Standaard |
| Trekspanning, jaar, type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Trekspanning, brk, type I, 50 mm/min | 63 | MPa | ASTM D 638 |
| Tensile strain, yld, type I, 50 mm/min | 6 | % | ASTM D 638 |
| Strekkingsspanning, brk, type I, 50 mm/min | 135 | % | ASTM D 638 |
| Tensielmodule, 5 mm/min | 2240 | MPa | ASTM D 638 |
| Flexurele spanning, jaar, 1,3 mm/min, 50 mm span | 98 | MPa | ASTM D 790 |
| Flexurale modulus, 1,3 mm/min, 50 mm overspanning | 2220 | MPa | ASTM D 790 |
| Hardheid, Rockwell R | 120 | - | ASTM D 785 |
| Tensiestress, rendement, 50 mm/min | 62 | MPa | ISO 527 |
| Trekspanning, breuk, 50 mm/min | 66 | MPa | ISO 527 |
| Tensile spanning, opbrengst, 50 mm/min | 6 | % | ISO 527 |
| Tensile spanning, breuk, 50 mm/min. | 124 | % | ISO 527 |
| Tensielmodule, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexurele spanning, rendement, 2 mm/min | 90 | MPa | ISO 178 |
| Flexurale modulus, 2 mm/min | 2120 | MPa | ISO 178 |
| INKOMST | Waarde | Eenheid | Standaard |
| Izod Impact, gesnoept, 23°C | 887 | J/m | ASTM D 256 |
| Izod Impact, gesnoept, -10°C | 838 | J/m | ASTM D 256 |
| Izod Impact, ingekapst, -30°C | 145 | J/m | ASTM D 256 |
| Multiaxiale impact | 116 | J | ISO 6603 |
| Totale energie van de instrumenteninslag, 23°C | 76 | J | ASTM D 3763 |
| Izod Impact, ongeboorde 80*10*3 +23°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ongeboord 80*10*3 -30°C | NB: | kJ/m2 | ISO 180/1U |
| Izod Impact, ingekerfd 80*10*3 +23°C | 67 | kJ/m2 | ISO 180/1A |
| Izod Impact, ingekerfd 80*10*3 -30°C | 22 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 79 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 14 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*3 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB: | kJ/m2 | ISO 179/1eU |
| Termiek | Waarde | Eenheid | Standaard |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 136 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, niet gegrild | 123 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, niet gegoten | 113 | °C | ASTM D 648 |
| CTE, -40°C tot 40°C, stroom | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C tot 40°C, stroom | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C tot 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Boldrukonderzoek, 125°C +/- 2°C | Passing | - | IEC 60695-10-2 |
| Vicat-verzachtingstemperatuur, snelheid B/50 | 129 | °C | ISO 306 |
| Vicat verzachtingstemperatuur, snelheid B/120 | 130 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 115 | °C | ISO 75/Af |
| FYSISCHE | Waarde | Eenheid | Standaard |
| Specifieke zwaarte | 1.2 | - | ASTM D 792 |
| Dichtheid | 1.2 | g/cm3 | ASTM D 792 |
| Schimmelkrimp, doorstroming, 3,2 mm (5) | 0.5 tegen 0.7 | % | S-Plastics-methode |
| Smeltstroom, 300°C/1,2 kgf | 18 | g/10 min | ASTM D 1238 |
| Dichtheid | 1.2 | g/cm3 | ISO 1183 |
| Absorptie van water (23°C/sat) | 0.3 | % | ISO 62 |
| Vochtabsorptie (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Smeltvolume, MVR bij 300°C/1,2 kg | 17 | cm3/10 min | ISO 1133 |
| Optische | Waarde | Eenheid | Standaard |
| Lichttransmissie, 2,54 mm | 88 | % | ASTM D 1003 |
| Nevel, 2,54 mm | < 1 | % | ASTM D 1003 |
| Brekingsindex | 1.582 | - | ASTM D 542 |
| Bron GMD, voor het laatst bijgewerkt:2010/02/28 | |||
| Parameter | ||
| Injectievorming | Waarde | Eenheid |
| Droogtemperatuur | 120 | °C |
| Droogtijd | 3 - 4 | uur |
| Droogtijd (cumulatief) | 48 | uur |
| Maximaal vochtgehalte | 0.02 | % |
| Smelttemperatuur | 295 - 315 | °C |
| Temperatuur van het spuitstuk | 290 - 310 | °C |
| Voorkant - Temperatuur in zone 3 | 295 - 315 | °C |
| Midden - Temperatuur van zone 2 | 280 - 305 | °C |
| Temperatuur achterin zone 1 | 270 - 295 | °C |
| Schimmeltemperatuur | 70 - 95 | °C |
| Achterdruk | 0.3 - 0.7 | MPa |
| Schroefsnelheid | 40 - 70 | rpm |
| Schot naar cilindergrootte | 40 - 60 | % |
| Afluchtsdiepte | 0.025 - 0.076 | mm |
| Bron GMD, voor het laatst bijgewerkt:2010/02/28 | ||
|
Voor meer informatie downloadt u het gegevensblad |
|
 |